TīmeklisFe-ZSM-5 with a SiO 2 : Al 2 O 3 ratio of (28 : 1) and a Fe content of 0.06–3 wt% have been prepared using a hydrothermal synthesis methodology, with a similar procedure also utilised for the Fe-free analogue. The procedure to produce the 1%Fe-ZSM-5 catalyst is outlined below. Tīmeklis2024. gada 15. dec. · To characterize the chemical state of Fe centers in ZSM-5, X-ray photoelectron spectroscopy (XPS; Thermal ESCALAB 250) is performed by using Al …
Active sites for NO reduction over Fe-ZSM-5 catalysts
TīmeklisFe–ZSM-5 was produced from H–ZSM-5 by solid-state exchange using the following procedure. Four grams of NH 4–ZSM-5 was calcined as described above. After8hat 823 K, the air flow was stopped and the reactor was purged at 823 K for 1 h with a 50 cm3/min flow of helium. The reactor was then cooled to room temperature in helium … Tīmeklis2024. gada 4. maijs · ZSM-5 was metal modified using different loadings (0.5–5 wt%) of Fe and Cr via the impregnation method. The metal modified ZSM-5 samples are compared and the effect of metal loading on the physicochemical properties and catalytic performance is investigated. state 2 human features of the sahel region
Encapsulation of ultra-small Cu–Fe into ZSM-5 zeolites for NH3
Tīmeklis2024. gada 1. janv. · The as-prepared Cu–Fe-ZSM-5 zeolite catalysts exhibit outstanding catalytic performance for NH 3 -SCR in the broad temperature windows of 220–480 °C. Moreover, they also display high stability and good resistance to H 2 CRediT authorship contribution statement Tīmeklis2024. gada 24. aug. · Fe-ZSM-5 catalysts modified by Cu and Ce by aqueous solution ion-exchange and incipient wetness impregnation methods were tested in the selective catalytic reduction of NOx with NH3. A variety of characterization techniques (NH3-SCO, BET, XRD, XPS, UV-Vis, NH3-TPD, H2-TPR) were used to explore the changes of … Tīmeklis2024. gada 10. marts · Fe-ZSM-5 zeolite for efficient removal of basic Fuchsin dye from aqueous solutions: Synthesis, characterization and adsorption process optimization … state 2 laws of chemical combination